ABSTRACT Objectives: To evaluate the translucency, contrast ratio and masking ability of a translucent zirconia with different thicknesses. Methods: Disc shaped specimens (n= 3) with 10 mm (Ø) x 1.5 mm, 1 mm and 0.7 mm (thickness) were manufactured simulating all-ceramic simplified restorations. Substrate discs (n= 2; Ø: 10 mm; thickness: 2 mm) were simulated with composite resin shades: A2 (positive control) and C4; and metal alloys: silver (Ni-Cr) and golden (Cu-Al). Optical properties of the 9 translucent zirconia specimens placed on the 3 different substrates were analyzed by a spectrophotometer. The color variation (ΔE00) between each ceramic structure over the positive control substrate (A2) and over the dark backgrounds (C4, silvery, golden) were obtained as to their ceramic masking ability and subjected to non-parametric Kruskal Wallis test (5%). The translucency parameter (TP00) and contrast ratio (CR) of the different thicknesses of the ceramic discs were also collected and analyzed by one-way ANOVA and the Tukey test (5%). Results: The translucent zirconia showed greater opacity in the thickness of 1.5 mm, although it was not statistically different between 0.7 and 1.0 mm. All dark backgrounds significantly affected the final color of the simplified restoration in all evaluated thicknesses. However, the increase in ceramic thickness showed a decrease in ΔE00 values for all substrates. Conclusion: The translucent zirconia was not able to mask the dark substrates, independent of the evaluated thickness.

RESUMO Objetivos: Avaliar a translucidez, razão de contraste e capacidade de mascaramento de uma zircônia translúcida com diferentes espessuras. Métodos: Espécimes em forma de disco (n= 3) com 10 mm (Ø) x 1,5 mm, 1 mm e 0,7 mm (espessura) foram confeccionados simulando restaurações simplificadas em cerâmica pura. Discos de substrato (n= 2; Ø: 10 mm; espessura: 2 mm) foram simulados com as cores de resina composta: A2 (controle positivo) e C4; e ligas metálicas: prata (Ni-Cr) e ouro (Cu-Al). As propriedades ópticas dos 9 espécimes de zircônia translúcida posicionados nos 3 substratos diferentes foram analisadas por um espectrofotômetro. A variação de cor (ΔE00) entre cada espécime cerâmico sobre o substrato controle positivo (A2) e sobre os fundos escuros (C4, prateado, dourado) foi calculada quanto à capacidade de mascaramento da cerâmica e submetida ao teste não paramétrico de Kruskal Wallis (5%). O parâmetro de translucidez (TP00) e a razão de contraste (CR) das diferentes espessuras dos discos cerâmicos também foram coletados e analisados por ANOVA de uma via e teste de Tukey (5%). Resultados: A zircônia translúcida apresentou maior opacidade na espessura de 1,5 mm, embora não tenha sido estatisticamente diferente entre 0,7 e 1,0 mm. Todos os fundos escuros afetaram significativamente a cor final da restauração simplificada em todas as espessuras avaliadas. No entanto, o aumento da espessura da cerâmica mostrou uma diminuição nos valores de ΔE00 para todos os substratos. Conclusão: A zircônia translúcida não foi capaz de mascarar os substratos escuros, independente da espessura avaliada.

Abstract This laboratory study aimed to evaluate the influence of endodontic sealer and cervical limit of root filling on the discoloration of root canal treated teeth. Bovine incisors were randomly distributed into six experimental groups and control (n=21/group), according to the endodontic sealer used [AH Plus (AP); MTA Fillapex (MF) and Sealer Plus BC (SPB)] and the cervical limit of root filling [dental cervix (DC) or 2 mm in apical direction (2mm-AD)]. Tooth discoloration (ΔE) was evaluated by a digital spectrophotometer using the CIED2000 method. Color assessments were performed immediately before (baseline), 1 week, 1, 3, 6 months, and 1 year after obturation. Data were analyzed by ANOVA and Tukey’s post-hoc tests (α=5%). Teeth filled with the three sealers showed perceptible tooth discoloration (ΔE≥2.7) in 1 week, maintaining similar values over time. There was a significant difference between MF and SPB sealers in the 2mm-AD groups. In addition, 2mm-AD groups promoted significantly lower discoloration than DC groups for AH (3 months) and SPB (1 and 3 months) sealer,s. Teeth filled with AP, MF, and SPB sealers displayed discoloration from 1 week to one year, with differences between MF and SPB sealers. A cervical limit of filling material at 2 mm from the dental cervix seems more advisable, promoting lower crown discoloration.

Resumo O presente estudo laboratorial teve como objetivo avaliar a influência do cimento endodôntico e do limite cervical da obturação radicular na alteração de cor de dentes tratados endodonticamente. Incisivos bovinos foram distribuídos aleatoriamente em seis grupos experimentais e um controle (n=21/grupo), de acordo com o cimento endodôntico utilizado [AH Plus (AP); MTA Fillapex (MF) e Sealer Plus BC (SPB)] e o limite cervical da obturação [Colo dentário (CD) ou 2mm na direção apical (2mm-DA)]. A alteração de cor (ΔE) foi avaliada por um espectofotômetro digital usando o método CIED2000. As avaliações de cor foram realizadas imediatamente antes (baseline), 1 semana, 1, 3, 6 meses e 1 ano após a obturação. Os dados foram analisados pelos testes ANOVA e post-hoc de Tuckey (α=5%). Dentes obturados com os três cimentos apresentaram alteração de cor perceptível (ΔE≥2.7) em 1 semana, mantendo valores semelhantes ao longo do tempo. Houve uma diferença significativa entre os cimentos MF e SPB nos grupos 2mm-DA. Além disso, os grupos 2mm-DA promoveram uma alteração de cor significativamente menor do que o grupos CD para os cimentos AH (3 meses) e SPB (1 e 3 meses). Os dentes obturados com os cimentos AH, MF e SPB apresentaram alteração de cor entre 1 semana a um ano, com diferenças entre os cimentos MF e SPB. O limite cervical do material obturador a 2mm do colo dentário parece mais aconselhável, promovendo menor alteração de cor da coroa dentária.

Aim This study assessed the color and translucency stability of a polymer infiltrated ceramic network (PICN) and compared it with a resin composite (RC) and a feldspathic ceramic (FEL). Methods Disc-shaped samples of a PICN (Vita Enamic), a feldspathic ceramic (Vitablocks Mark II), and a resin composite (Brava block) were prepared from CAD/CAM blocks. PICN and RC surfaces were finished with a sequence of polishing discs and diamond paste. FEL samples received a glaze layer. The samples were subjected to 30-min immersions in red wine twice a day for 30 days. CIE L*a*b* coordinates were assessed with a spectrophotometer at baseline and after 15 and 30 days of immersion. Color alteration (∆E 00 ) and translucency parameter (TP 00 ) were calculated with CIEDE2000. Average roughness was measured before the staining procedures. Color difference and translucency data were analyzed with repeated-measures ANOVA and Tukey’s tests. Roughness was analyzed with the Kruskal-Wallis test. Results Roughness was similar among the experimental groups. All materials had their color alteration significantly increased from 15 to 30 days of staining. PICN reached an intermediate ∆E 00 between FEL and RC at 15 days. PICN revealed a color alteration as high as the composite after 30 days. No statistical difference was observed regarding translucency. Conclusion PICN was not as color stable as the feldspathic ceramic at the end of the study. Its color alteration was comparable to the resin composite when exposed to red wine. However, the translucency of the tested materials was stable throughout the 30-day staining.

Resumo O presente estudo objetivou investigar a influência do ambiente de teste no comportamento a fadiga estática (resistência à fratura e tempo para falha) de cerâmicas à base de dissilicato de lítio (LD) e zircônia estabilizada com ítria (YSZ). Espécimes de LD (IPS e.max CAD, Ivoclar Vivadent) e YSZ (IPS e.max ZirCAD MO, 3mol% Y2O3, Ivoclar Vivadent) foram obtidos e alocados aleatoriamente em três grupos: testado em ar, em líquido inerte (óleo de parafina) ou em água destilada. O teste de fadiga estática (n= 15) foi realizado usando o teste pistão sobre três esferas, ISO 6872, da seguinte forma: carga inicial 100 N para LD e 300 N para YSZ; tempo de aplicação de carregamento definido para 1 hora para cada etapa de carregamento; tamanho do passo de 50 N para LD e 100 N para YSZ, aplicados sucessivamente até a fratura. Dados de resistência à fadiga estática (MPa) e tempo até a fratura (horas) foram registrados. A análise fractográfica foi executada. A análise de sobrevivência corrobora a ausência de influência do ambiente de teste nos resultados de fadiga estática (resistência à fadiga, tempo de fratura e taxas de sobrevivência) para a YSZ. Para LD, os corpos de prova testados em ar apresentaram taxa de sobrevivência e resistência à fadiga estática estatisticamente superiores (p= 0,025). Em relação ao tempo de fratura, os espécimes LD testados em ar foram superiores aos testados em água destilada (p= 0,019) ou em ambiente inerte (p= 0,017). Não foram observadas diferenças estatísticas para o módulo de Weibull. Todas as falhas começaram no lado onde se concentra a tensão de tração (lado de baixo) durante o teste. Com base nisso, observa-se que o ambiente de teste não afetou os mecanismos de crescimento lento de trinca durante o teste de fadiga estática da cerâmica YSZ, mas desempenha um papel significativo na resistência à fadiga estática da cerâmica de vidro à base de dissilicato de lítio, indicando alta susceptibilidade ao crescimento lento e subcrítico de trincas.

Abstract It aims on evaluate the effect of the test environment on static fatigue behavior of lithium disilicate-based (LD), and yttrium oxide-stabilized zirconia (YSZ) ceramics. Specimens of LD (IPS e.max CAD, Ivoclar Vivadent) and YSZ (IPS e.max ZirCAD MO, 3 mol% Y2O3, Ivoclar Vivadent) were randomly allocated into three groups: tested in air, inert (paraffin oil, Sigma Aldrich) or distilled water. The static fatigue test (n=15) was performed using a piston-on-three ball assembly, adapted from ISO 6872, as follows: starting load 100 N for LD and 300 N for YSZ; loading application time set to 1 hour for each loading step; step size of 50 N for LD and 100 N for YSZ, applied successively until fracture. Data from static fatigue strength (MPa) and time to fracture (hours) were recorded. Fractographic analysis was executed. Survival analysis corroborates absence of influence of environment on static fatigue outcomes (fatigue strength, time to fracture and survival rates) for YSZ. For LD, specimens tested in air presented statistically superior survival rate and static fatigue strength (p= 0.025). In regards of time to fracture, LD tested in air were superior than when tested in distilled water (p=0.019) or inert (p=0.017) environments. No statistical differences for Weibull modulus were observed. Failures started on the tensile stress surface. Thus, the test environment did not affect slow crack growth (SCG) mechanisms during static fatigue test of YSZ ceramics, but it plays a significant role for the static fatigue behavior of lithium disilicate-based glass ceramics, indicating a high susceptibility to SCG.